Water based fluororesin non-stick mold coating PF-602

这里可以自定义设置
Water based fluororesin non-stick mold coating PF-602
Carbon steel cake mold pan non-stick ceramic coating
Water based fluororesin non-stick mold coating PF-602 is designed for metal mold coating. It has excellent non-stick performance, good heat resistant and abrasion resistant. It can be used for aluminum, steel and other metal mold coating.
B站不支持收货地址
B站不支持库存规格
Model
PF-602
MOQ
200kg
Payment
L/C, D/A, D/P, T/T, Western Union, MoneyGram, OA
Place of Origin
China Anhui
Brand
sinogracechist
参数暂无数据
多属性暂无数据
B站不支持优惠卷

Add success, do you want to check your shopping cart?

暂无分享
B站不支持产品保障
该产品后台详情无内容

Teflon Coatings PF-602 Water based fluororesin non-stick mold coating

Description

PF-602 is designed for metal mold coating. It has excellent non-stick performance, good heat resistant and abrasion resistant. It can be used for aluminum, steel and other metal mold coating.

Typical Properties

Type

Water based fluororesin

Appearance

Liquid (Customized color)

Solid content (%)

33±1 (Primer) 

35±1 (Top)

Viscosity (cp)

500~900 Primer 400~750Top

Density (g/ml)

1.28 Primer/1.30 Top

PH

8-11(Primer and top)

Color of the film surface

Flat and smooth

Curing temperature (℃)

380-420

Gloss (60° glossimeter)

15-25

Film thickness (μm)

20-35

Non-stick performance Fry eggs at 170±10℃

>10 cycles

Corrosion resistance Boling 10% salt water for 24 hours

No blister

Abrasion resistance 3KG/21cm2

>4000 cycles

Hardness (ZHONGHUA pencil)

>H

Key Features

● PFOA free
● Excellent non-stick performance and heat resistant 
● Excellent chemical resistance and abrasive resistance
● Excellent and lasting non-stick performance, easy to clean

APPLICATION

● Aluminum, steel and other metal mold coating

这里可以自定义设置

Storage and Handling

How to use

1. Requirement on pre-treatment

● Firstly, apply high-temperature degreasing, then wash with 1%~3% NaOH solution (60℃) for more than 6 minutes, dry it after water rinsing;
● Blast with 80#~120# corundum to make the surface roughness reach 2.0μ~3.0μ, pay attention to sandblast evenly;
● Wash with 1%~3% NaOH solution(60℃) for more than 6 minutes, rinse with water;
● Wash with 1%~3% hydrochloric acid solution (60℃) for more than 6 minutes, rinse with water and dry.

2.Preparation of the coating

● Dispersion of coating: the coating must be fully dispersed before operation;
● Viscosity adjustment: the viscosity could be adjusted according to different spray methods. Dilute with clean water if the viscosity is over high;
● Coating filtration: filtrate the coating with screen (100mesh) before using.

3.Application

● The spraying environment should be dry, well-ventilated, no smoking and fire. We suggest using dedicated spray gun, elevated tank and curing oven;
● The air compressor should be degreased, dewatered and equipped with water oil separator before using;
● Roll the coating at 30rpm speed before using to make sure there is no sediment, and filter with 100 mesh screen;
● Adjust atomization and oil pump capacity of the spraying gun; make sure the unit is clean and flat;
● Preheat the substrate to 35℃ and spray the primer. Dry it at temperature of 120℃~150℃ for 10min-15min. Keep the thickness of primer within 12μm-18μm;
● Spray top coating after the primer is dry and cooling to room temperature, then spray the top. Dry the unit at the temperature of 100℃~150℃ for 10~20 min, and gradually increase the temperature to 380℃~420℃. Keep for 10 min. Keep the thickness of top coat within 10μm~12μm. The thickness of two coat tally should be between 20μm~30μm;
● The oven (or the tunnel drier) must be well ventilated; otherwise, it will lead to color change of coating.